| Titre : | Conversion of ceramic UO2 pellets for HTR - 10 Fuel elements into nitrate with N2O4 (2011) |
| Auteurs : | Liyang Zhu, Auteur ; Wuhua Duan, Auteur ; Jingming Xu, Auteur |
| Type de document : | Article : texte imprimé |
| Dans : | Industrial & engineering chemistry research (Vol. 49 N° 22, Novembre 2010) |
| Article en page(s) : | pp. 11195–11199 |
| Note générale : | Chimie industrielle |
| Langues : | Anglais |
| Tags : | Ceramic Pellets |
| Résumé : | A 10 MW high-temperature gas-cooled reactor (HTR-10) has been constructed in China. It is important to study reprocessing of spent nuclear fuel from high-temperature gas-cooled reactor (HTGR) for recovery of nuclear resource and reduction of nuclear waste. Ceramic UO2 pellets of 0.5 mm in diameter for HTR-10 fuel elements were converted into nitrate with N2O4. When the molar ratio of water to uranium was 6, the conversion efficiency was above 99% after 180 min at 80 °C, and the conversion product was a mixture of UO2(NO3)2·3H2O and UO2(NO3)2·6H2O. When ceramic UO2 pellets were transformed to U3O8 powder with a particle size below 100 μm under an O2 stream and high temperature, the U3O8 powder was quickly converted into nitrate with N2O4 within 45 min. Water showed a significant effect on the reaction of U3O8 powder with N2O4, whereas other operation conditions had little effect on the reaction. |
| DEWEY : | 660 |
| ISSN : | 0888-5885 |
| En ligne : | http://pubs.acs.org/doi/abs/10.1021/ie101325n |