Effect of addition of N on L10 transformation and atomic diffusion in FePt films / V. Phatak in Acta materialia, Vol. 58 N° 3 (Fevrier 2010)  

Public ISBD [article]  inActa materialia > Vol. 58 N° 3 (Fevrier 2010) . - pp. 979-988 Titre : Effect of addition of N on L10 transformation and atomic diffusion in FePt films Type de document : texte imprimé Auteurs : V. Phatak, Auteur ; A. Gupta, Auteur ; V. R. Reddy, Auteur Article en page(s) : pp. 979-988 Note générale : Métallurgie Langues : Anglais (eng) Mots-clés : L10 transformation Self-diffusion Nuclear resonance reflectivity Secondary ion mass spectrometry Index. décimale : 669 Métallurgie Résumé : The effect of nitrogen incorporation on the kinetics of L10 transformation in FePt alloy films was studied. Films with a maximum possible amount of nitrogen were prepared by sputtering a FePt compound target with pure nitrogen. As-prepared films consisting of nano-grains of Pt and Fe0.7N0.3 transformed to face-centered cubic FePt phase with a certain amount of nitrogen incorporated in the grains after annealing at 573 K. It was found that the presence of N results in faster kinetics of L10 transformation compared with pure FePt alloy films, as well as a substantial reduction in grain size. Detailed structural and diffusion measurements were carried out to elucidate the mechanism of enhanced transformation kinetics as well as grain size reduction. The activation energy for volume diffusion of Fe in FePtN films was found to be 0.27 ± 0.14 eV, while that in FePt was 0.50 ± 0.17 eV. Faster atomic diffusion in nitrogen-containing films was the cause of an enhanced rate of L10 transformation. Further studies reveal that, in partially transformed FePtN alloy films, N is incorporated mainly in the grain boundary region, which hinders grain growth and results in a smaller grain size. DEWEY : 669 ISSN : 1359-6454 En ligne : http://www.sciencedirect.com/science?_ob=PublicationURL&_tockey=%23TOC%235556%23 [...] [article] Effect of addition of N on L10 transformation and atomic diffusion in FePt films [texte imprimé] / V. Phatak, Auteur ; A. Gupta, Auteur ; V. R. Reddy, Auteur . - pp. 979-988. Métallurgie Langues : Anglais (eng) in Acta materialia > Vol. 58 N° 3 (Fevrier 2010) . - pp. 979-988 Mots-clés : L10 transformation Self-diffusion Nuclear resonance reflectivity Secondary ion mass spectrometry Index. décimale : 669 Métallurgie Résumé : The effect of nitrogen incorporation on the kinetics of L10 transformation in FePt alloy films was studied. Films with a maximum possible amount of nitrogen were prepared by sputtering a FePt compound target with pure nitrogen. As-prepared films consisting of nano-grains of Pt and Fe0.7N0.3 transformed to face-centered cubic FePt phase with a certain amount of nitrogen incorporated in the grains after annealing at 573 K. It was found that the presence of N results in faster kinetics of L10 transformation compared with pure FePt alloy films, as well as a substantial reduction in grain size. Detailed structural and diffusion measurements were carried out to elucidate the mechanism of enhanced transformation kinetics as well as grain size reduction. The activation energy for volume diffusion of Fe in FePtN films was found to be 0.27 ± 0.14 eV, while that in FePt was 0.50 ± 0.17 eV. Faster atomic diffusion in nitrogen-containing films was the cause of an enhanced rate of L10 transformation. Further studies reveal that, in partially transformed FePtN alloy films, N is incorporated mainly in the grain boundary region, which hinders grain growth and results in a smaller grain size. DEWEY : 669 ISSN : 1359-6454 En ligne : http://www.sciencedirect.com/science?_ob=PublicationURL&_tockey=%23TOC%235556%23 [...]

Exemplaires

Code-barres	Cote	Support	Localisation	Section	Disponibilité
aucun exemplaire

Effect of addition of N on L10 transformation and atomic diffusion in FePt films / V. Phatak in Acta materialia, Vol. 58 N° 3 (Fevrier 2010)  

Public ISBD [article]  inActa materialia > Vol. 58 N° 3 (Fevrier 2010) . - pp. 979–988 Titre : Effect of addition of N on L10 transformation and atomic diffusion in FePt films Type de document : texte imprimé Auteurs : V. Phatak, Auteur ; A. Gupta, Auteur ; V. R. Reddy, Auteur Année de publication : 2011 Article en page(s) : pp. 979–988 Note générale : Métallurgie Langues : Anglais (eng) Mots-clés : L10 transformation Self-diffusion Nuclear resonance reflectivity Secondary ion mass spectrometry Résumé : The effect of nitrogen incorporation on the kinetics of L10 transformation in FePt alloy films was studied. Films with a maximum possible amount of nitrogen were prepared by sputtering a FePt compound target with pure nitrogen. As-prepared films consisting of nano-grains of Pt and Fe0.7N0.3 transformed to face-centered cubic FePt phase with a certain amount of nitrogen incorporated in the grains after annealing at 573 K. It was found that the presence of N results in faster kinetics of L10 transformation compared with pure FePt alloy films, as well as a substantial reduction in grain size. Detailed structural and diffusion measurements were carried out to elucidate the mechanism of enhanced transformation kinetics as well as grain size reduction. The activation energy for volume diffusion of Fe in FePtN films was found to be 0.27 ± 0.14 eV, while that in FePt was 0.50 ± 0.17 eV. Faster atomic diffusion in nitrogen-containing films was the cause of an enhanced rate of L10 transformation. Further studies reveal that, in partially transformed FePtN alloy films, N is incorporated mainly in the grain boundary region, which hinders grain growth and results in a smaller grain size. DEWEY : 669 ISSN : 1359-6454 En ligne : http://www.sciencedirect.com/science/article/pii/S1359645409006934 [article] Effect of addition of N on L10 transformation and atomic diffusion in FePt films [texte imprimé] / V. Phatak, Auteur ; A. Gupta, Auteur ; V. R. Reddy, Auteur . - 2011 . - pp. 979–988. Métallurgie Langues : Anglais (eng) in Acta materialia > Vol. 58 N° 3 (Fevrier 2010) . - pp. 979–988 Mots-clés : L10 transformation Self-diffusion Nuclear resonance reflectivity Secondary ion mass spectrometry Résumé : The effect of nitrogen incorporation on the kinetics of L10 transformation in FePt alloy films was studied. Films with a maximum possible amount of nitrogen were prepared by sputtering a FePt compound target with pure nitrogen. As-prepared films consisting of nano-grains of Pt and Fe0.7N0.3 transformed to face-centered cubic FePt phase with a certain amount of nitrogen incorporated in the grains after annealing at 573 K. It was found that the presence of N results in faster kinetics of L10 transformation compared with pure FePt alloy films, as well as a substantial reduction in grain size. Detailed structural and diffusion measurements were carried out to elucidate the mechanism of enhanced transformation kinetics as well as grain size reduction. The activation energy for volume diffusion of Fe in FePtN films was found to be 0.27 ± 0.14 eV, while that in FePt was 0.50 ± 0.17 eV. Faster atomic diffusion in nitrogen-containing films was the cause of an enhanced rate of L10 transformation. Further studies reveal that, in partially transformed FePtN alloy films, N is incorporated mainly in the grain boundary region, which hinders grain growth and results in a smaller grain size. DEWEY : 669 ISSN : 1359-6454 En ligne : http://www.sciencedirect.com/science/article/pii/S1359645409006934

Exemplaires

Code-barres	Cote	Support	Localisation	Section	Disponibilité
aucun exemplaire