Surfactant assisted hydrothermal and thermal decomposition synthesis of alumina microfibers with mesoporous structure / Zhenfeng Zhu in Chemical engineering journal, Vol. 155 N° 3 (Decembre 2009) 

Public ISBD [article]  in Chemical engineering journal > Vol. 155 N° 3 (Decembre 2009) . - pp. 925-930 Titre : Surfactant assisted hydrothermal and thermal decomposition synthesis of alumina microfibers with mesoporous structure Type de document : texte imprimé Auteurs : Zhenfeng Zhu, Auteur ; Hui Liu, Auteur ; Hongjun Sun, Auteur Année de publication : 2010 Article en page(s) : pp. 925-930 Note générale : Génie Chimique Langues : Anglais (eng) Mots-clés : Mesoporous  alumina  Microfibers  Hydrothermal  synthesis  SCR-NH3  of  NO Index. décimale : 660 Résumé : The alumina microfibers with mesoporous structure were synthesized by a facile hydrothermal and thermal decomposition route. The as-obtained products were well characterized by XRD, SEM, TEM (HRTEM), SAED and N2 adsorption–desorption measurement. It was shown that the length and diameter of these alumina microfibers are about 10 μm and 300–500 nm, respectively. All these alumina microfibers prepared by the PEG templates with different molecular weight have the different high surface area but nearly the same pore diameter about 3.5 nm. The calcination experimental result shows that the mesoporosity of these alumina microfibers can be maintained even at 1373 K. On the other hand, the higher selective catalytic reduction (SCR) of NO effectiveness present that the as-obtained mesoporous alumina have stronger adsorption property because of its high surface area. DEWEY : 660 ISSN : 1385-8947 En ligne : http://www.sciencedirect.com/science?_ob=ArticleURL&_udi=B6TFJ-4X9NVBP-4&_user=6 [...] [article] Surfactant assisted hydrothermal and thermal decomposition synthesis of alumina microfibers with mesoporous structure [texte imprimé] / Zhenfeng Zhu, Auteur ; Hui Liu, Auteur ; Hongjun Sun, Auteur . - 2010 . - pp. 925-930. Génie Chimique Langues : Anglais (eng) in Chemical engineering journal > Vol. 155 N° 3 (Decembre 2009) . - pp. 925-930 Mots-clés : Mesoporous  alumina  Microfibers  Hydrothermal  synthesis  SCR-NH3  of  NO Index. décimale : 660 Résumé : The alumina microfibers with mesoporous structure were synthesized by a facile hydrothermal and thermal decomposition route. The as-obtained products were well characterized by XRD, SEM, TEM (HRTEM), SAED and N2 adsorption–desorption measurement. It was shown that the length and diameter of these alumina microfibers are about 10 μm and 300–500 nm, respectively. All these alumina microfibers prepared by the PEG templates with different molecular weight have the different high surface area but nearly the same pore diameter about 3.5 nm. The calcination experimental result shows that the mesoporosity of these alumina microfibers can be maintained even at 1373 K. On the other hand, the higher selective catalytic reduction (SCR) of NO effectiveness present that the as-obtained mesoporous alumina have stronger adsorption property because of its high surface area. DEWEY : 660 ISSN : 1385-8947 En ligne : http://www.sciencedirect.com/science?_ob=ArticleURL&_udi=B6TFJ-4X9NVBP-4&_user=6 [...]