Documents disponibles écrits par cet auteur

Relationships between rolled grain shape, deformation bands, microstructures and recrystallization textures in Al–5%Mg / C. S. T. Chang in Acta materialia, Vol. 58 N° 2 (Janvier 2010) 

Public ISBD [article]  in Acta materialia > Vol. 58 N° 2 (Janvier 2010) . - pp. 476-489 Titre : Relationships between rolled grain shape, deformation bands, microstructures and recrystallization textures in Al–5%Mg Type de document : texte imprimé Auteurs : C. S. T. Chang, Auteur ; B. J. Duggan, Auteur Article en page(s) : pp. 476-489 Note générale : Métallurgie Langues : Anglais (eng) Mots-clés : Rolling  Recrystallization  texture  Shear  bands  Electron  backscattering  patterns  (EBSP)  Aluminium  alloys Index. décimale : 669 Métallurgie Résumé : In this study, the textures and microstructures of Al–5%Mg after cold rolling 95% and recrystallization at 300 and 450°C have been investigated. The cold rolling textures were typical but the recrystallization textures at 300°C comprised Cube and S and at 450 °C, Cube, ND Rotated Cube plus a weak Q component. The deformed grains were wavy in the longitudinal section as a result of composite-like behaviour, and the narrowed regions had scattered orientations which weakened the final annealing texture. Another feature was grains dividing into their respective crystallographic complements. S grains frequently behaved in this way and nucleation of S-oriented recrystallized material at low temperature was common. Cube-oriented volumes were often found between complementary S volumes, and this favoured micro-growth selection and a detailed discussion of the Cube origins are given. Remarkably, recrystallization texture is largely determined by the behaviour of S- and Cube-oriented material. DEWEY : 669 ISSN : 1359-6454 En ligne : http://www.sciencedirect.com/science?_ob=PublicationURL&_tockey=%23TOC%235556%23 [...] [article] Relationships between rolled grain shape, deformation bands, microstructures and recrystallization textures in Al–5%Mg [texte imprimé] / C. S. T. Chang, Auteur ; B. J. Duggan, Auteur . - pp. 476-489. Métallurgie Langues : Anglais (eng) in Acta materialia > Vol. 58 N° 2 (Janvier 2010) . - pp. 476-489 Mots-clés : Rolling  Recrystallization  texture  Shear  bands  Electron  backscattering  patterns  (EBSP)  Aluminium  alloys Index. décimale : 669 Métallurgie Résumé : In this study, the textures and microstructures of Al–5%Mg after cold rolling 95% and recrystallization at 300 and 450°C have been investigated. The cold rolling textures were typical but the recrystallization textures at 300°C comprised Cube and S and at 450 °C, Cube, ND Rotated Cube plus a weak Q component. The deformed grains were wavy in the longitudinal section as a result of composite-like behaviour, and the narrowed regions had scattered orientations which weakened the final annealing texture. Another feature was grains dividing into their respective crystallographic complements. S grains frequently behaved in this way and nucleation of S-oriented recrystallized material at low temperature was common. Cube-oriented volumes were often found between complementary S volumes, and this favoured micro-growth selection and a detailed discussion of the Cube origins are given. Remarkably, recrystallization texture is largely determined by the behaviour of S- and Cube-oriented material. DEWEY : 669 ISSN : 1359-6454 En ligne : http://www.sciencedirect.com/science?_ob=PublicationURL&_tockey=%23TOC%235556%23 [...]