Documents disponibles écrits par cet auteur

Preparation and characterization of sulfonated copolyamides based on poly(hexafluoroisopropylidene) isophthalamides for polymer electrolytic membranes / Yamile Perez-Padilla in Industrial & engineering chemistry research, Vol. 50 N° 16 (Août 2011) 

Public ISBD [article]  in Industrial & engineering chemistry research > Vol. 50 N° 16 (Août 2011) . - pp. 9617-9624 Titre : Preparation and characterization of sulfonated copolyamides based on poly(hexafluoroisopropylidene) isophthalamides for polymer electrolytic membranes Type de document : texte imprimé Auteurs : Yamile Perez-Padilla, Auteur ; Mascha. A. Smit, Auteur ; Manuel J. Aguilar-Vega, Auteur Année de publication : 2011 Article en page(s) : pp. 9617-9624 Note générale : Chimie industrielle Langues : Anglais (eng) Mots-clés : Preparation  Polymer  electrolytic  membranes Résumé : A series of sulfonated random copolyamides with increasing sulfonation degree were synthesized from the aromatic diamine 4,4'-(hexafluoroisopropylidene)dianiline, HFA, reacted with 2,4-diaminobenzenosulfonic acid, DABS, by direct polycondensation using isophthalic diacid, ISO, as comonomer. Thin films of the sulfonated copolyamides were prepared by the solution-evaporation method using dimethylacetamide, DMAc. The structure of the resulting sulfonated copolyamides was confirmed by FTIR and 1H NMR which evidenced the presence of amide and sulfonic groups in the proposed concentrations. Thermal stabilities as characterized by TGA, showed the onset of decomposition at 320 °C for the ionic moieties and above 600 °C for the nonsulfonated part of the copolymers. The values of water uptake and ion exchange capacity, IEC, at room temperature for the copolymer with 50 mol % of DABS, HFAS55 membrane were higher than those obtained for Nafion 115. HFAS55 also presented a proton conductivity value of 3.3 (mS cm―1) which was similar to the one of Nafion 115 tested under the same conditions which situates it as a possible material for PEM membrane preparation. DEWEY : 660 ISSN : 0888-5885 En ligne : http://cat.inist.fr/?aModele=afficheN&cpsidt=24425205 [article] Preparation and characterization of sulfonated copolyamides based on poly(hexafluoroisopropylidene) isophthalamides for polymer electrolytic membranes [texte imprimé] / Yamile Perez-Padilla, Auteur ; Mascha. A. Smit, Auteur ; Manuel J. Aguilar-Vega, Auteur . - 2011 . - pp. 9617-9624. Chimie industrielle Langues : Anglais (eng) in Industrial & engineering chemistry research > Vol. 50 N° 16 (Août 2011) . - pp. 9617-9624 Mots-clés : Preparation  Polymer  electrolytic  membranes Résumé : A series of sulfonated random copolyamides with increasing sulfonation degree were synthesized from the aromatic diamine 4,4'-(hexafluoroisopropylidene)dianiline, HFA, reacted with 2,4-diaminobenzenosulfonic acid, DABS, by direct polycondensation using isophthalic diacid, ISO, as comonomer. Thin films of the sulfonated copolyamides were prepared by the solution-evaporation method using dimethylacetamide, DMAc. The structure of the resulting sulfonated copolyamides was confirmed by FTIR and 1H NMR which evidenced the presence of amide and sulfonic groups in the proposed concentrations. Thermal stabilities as characterized by TGA, showed the onset of decomposition at 320 °C for the ionic moieties and above 600 °C for the nonsulfonated part of the copolymers. The values of water uptake and ion exchange capacity, IEC, at room temperature for the copolymer with 50 mol % of DABS, HFAS55 membrane were higher than those obtained for Nafion 115. HFAS55 also presented a proton conductivity value of 3.3 (mS cm―1) which was similar to the one of Nafion 115 tested under the same conditions which situates it as a possible material for PEM membrane preparation. DEWEY : 660 ISSN : 0888-5885 En ligne : http://cat.inist.fr/?aModele=afficheN&cpsidt=24425205