Tribological behavior of heat treated Ni-rich NiTi alloys / R. Aliasgarian in Transactions of the ASME . Journal of tribology, Vol. 133 N° 3 (Juillet 2011)  

Public ISBD [article]  inTransactions of the ASME . Journal of tribology > Vol. 133 N° 3 (Juillet 2011) . - 06 p. Titre : Tribological behavior of heat treated Ni-rich NiTi alloys Type de document : texte imprimé Auteurs : R. Aliasgarian, Auteur ; H. M. Ghasemi, Auteur ; M. Abedini, Auteur Année de publication : 2012 Article en page(s) : 06 p. Note générale : Tribology Langues : Anglais (eng) Mots-clés : Ageing Fracture toughness Hardness Nickel alloys Titanium Wear testing Index. décimale : 621.5 Energie pneumatique. Machinerie et outils. Réfrigération Résumé : Effects of heat treatments and applied loads on the tribological behavior of Ti-56.5 wt. % Ni and Ti-57.5 wt. % Ni alloys were investigated. Wear tests were performed on a pin-on-disk tribometer under normal loads of 20 N and 60 N at a sliding speed of 0.3 m/s. The results indicated that the alloys aged at 700 °C showed lower hardness comparing to the alloys aged at 400 °C. Under an applied load of 20 N, the samples aged at 700 °C showed better wear behavior in comparison with the samples aged at 400 °C with a higher hardness. This could be attributed to higher toughness of the samples aged at 700 °C. The results also showed that the wear of the samples aged at 400 °C decreased with the increase in normal load. However, there was an increase in the wear of the samples aged at 700 °C with the increase of load. Formation and stability of tribological layers on the contacting surfaces could be the main reason for the reduction of the wear of the samples aged at 400 °C with the increase in normal load. DEWEY : 621.5 ISSN : 0742-4787 En ligne : http://scitation.aip.org/getabs/servlet/GetabsServlet?prog=normal&id=JOTRE900013 [...] [article] Tribological behavior of heat treated Ni-rich NiTi alloys [texte imprimé] / R. Aliasgarian, Auteur ; H. M. Ghasemi, Auteur ; M. Abedini, Auteur . - 2012 . - 06 p. Tribology Langues : Anglais (eng) in Transactions of the ASME . Journal of tribology > Vol. 133 N° 3 (Juillet 2011) . - 06 p. Mots-clés : Ageing Fracture toughness Hardness Nickel alloys Titanium Wear testing Index. décimale : 621.5 Energie pneumatique. Machinerie et outils. Réfrigération Résumé : Effects of heat treatments and applied loads on the tribological behavior of Ti-56.5 wt. % Ni and Ti-57.5 wt. % Ni alloys were investigated. Wear tests were performed on a pin-on-disk tribometer under normal loads of 20 N and 60 N at a sliding speed of 0.3 m/s. The results indicated that the alloys aged at 700 °C showed lower hardness comparing to the alloys aged at 400 °C. Under an applied load of 20 N, the samples aged at 700 °C showed better wear behavior in comparison with the samples aged at 400 °C with a higher hardness. This could be attributed to higher toughness of the samples aged at 700 °C. The results also showed that the wear of the samples aged at 400 °C decreased with the increase in normal load. However, there was an increase in the wear of the samples aged at 700 °C with the increase of load. Formation and stability of tribological layers on the contacting surfaces could be the main reason for the reduction of the wear of the samples aged at 400 °C with the increase in normal load. DEWEY : 621.5 ISSN : 0742-4787 En ligne : http://scitation.aip.org/getabs/servlet/GetabsServlet?prog=normal&id=JOTRE900013 [...]

Exemplaires

Code-barres	Cote	Support	Localisation	Section	Disponibilité
aucun exemplaire