Selective dissolution of nanolamellar Ti–41 at.% Al alloy single crystals |
Type de document : |
texte imprimé |
Auteurs : |
Yuichiro Koizumi, Auteur ; Atsushi Sugihara, Auteur ; Hiroaki Tsuchiya, Auteur |
Année de publication : |
2011 |
Article en page(s) : |
pp. 2876–2886 |
Note générale : |
Métallurgie |
Langues : |
Anglais (eng) |
Mots-clés : |
Titanium aluminides Multilayers Nanostructure Corrosion Electrochemistry |
Résumé : |
The selective dissolution behavior of Ti–41 at.% Al single crystals having a α2/γ-lamellar structure with a lamellar thickness in the range 20 nm to 1 μm have been investigated in 0.5 M NaCl aqueous solution focusing on the effect of lamellar thickness on the dissolution of γ-lamellae. In the case where γ-lamellae were thicker than ∼100 nm on average, γ-lamellae were selectively dissolved and, as a result, crevasses whose widths were close to the γ-lamellae thicknesses were formed. However, not all γ-lamellae were dissolved and the distribution of crevasses was much less uniform compared with that of the γ-lamellae. On the other hand, when the average γ-lamellae thickness was |
DEWEY : |
669 |
ISSN : |
1359-6454 |
En ligne : |
http://www.sciencedirect.com/science/article/pii/S1359645410000303 |
in Acta materialia > Vol. 58 N° 8 (Mai 2010) . - pp. 2876–2886
[article] Selective dissolution of nanolamellar Ti–41 at.% Al alloy single crystals [texte imprimé] / Yuichiro Koizumi, Auteur ; Atsushi Sugihara, Auteur ; Hiroaki Tsuchiya, Auteur . - 2011 . - pp. 2876–2886. Métallurgie Langues : Anglais ( eng) in Acta materialia > Vol. 58 N° 8 (Mai 2010) . - pp. 2876–2886
Mots-clés : |
Titanium aluminides Multilayers Nanostructure Corrosion Electrochemistry |
Résumé : |
The selective dissolution behavior of Ti–41 at.% Al single crystals having a α2/γ-lamellar structure with a lamellar thickness in the range 20 nm to 1 μm have been investigated in 0.5 M NaCl aqueous solution focusing on the effect of lamellar thickness on the dissolution of γ-lamellae. In the case where γ-lamellae were thicker than ∼100 nm on average, γ-lamellae were selectively dissolved and, as a result, crevasses whose widths were close to the γ-lamellae thicknesses were formed. However, not all γ-lamellae were dissolved and the distribution of crevasses was much less uniform compared with that of the γ-lamellae. On the other hand, when the average γ-lamellae thickness was |
DEWEY : |
669 |
ISSN : |
1359-6454 |
En ligne : |
http://www.sciencedirect.com/science/article/pii/S1359645410000303 |
|