Thermodynamic evaluation of hypereutectic Al–Si (A390) alloy with addition of Mg / Alireza Hekmat-Ardakan in Acta materialia, Vol. 58 N° 9 (Mai 2010)  

Public ISBD [article]  inActa materialia > Vol. 58 N° 9 (Mai 2010) . - pp. 3422–3428 Titre : Thermodynamic evaluation of hypereutectic Al–Si (A390) alloy with addition of Mg Type de document : texte imprimé Auteurs : Alireza Hekmat-Ardakan, Auteur ; Frank Ajersch, Auteur Année de publication : 2011 Article en page(s) : pp. 3422–3428 Note générale : Métallurgie Langues : Anglais (eng) Mots-clés : Thermodynamic Factsage Aluminum alloys Eutectic solidification Magnesium Résumé : This paper presents the thermodynamic evaluation of A390 hypereutectic Al–Si alloy (Al–17% Si–4.5% Cu–0.5% Mg) and alloys up to 10% Mg, using the Factsage® software. Two critical compositions were detected at 4.2% and 7.2% Mg where the temperatures of the liquidus, the start of the binary and of the ternary eutectic reaction are changed. These critical compositions show differences in the formation of Mg2Si intermetallic particles during the solidification interval. For compositions up to 4.2% Mg, the Mg2Si intermetallic phase first appears in the ternary eutectic zone. With Mg contents between 4.2% and 7.2%, Mg2Si particle appears in both the binary and ternary eutectic reactions. Above 7.2% Mg, it solidifies as a primary phase and also during the binary and ternary reactions. The calculated liquid fraction vs. temperature curves also showed a decrease of the eutectic formation temperature (knee point temperature) with the addition of Mg content up to 4.2% Mg. This temperature becomes almost constant up to 10% Mg. The calculation of eutectic formation temperature shows a good agreement with differential scanning calorimetry (DSC) tests. DEWEY : 669 ISSN : 1359-6454 En ligne : http://www.sciencedirect.com/science/article/pii/S1359645410001035 [article] Thermodynamic evaluation of hypereutectic Al–Si (A390) alloy with addition of Mg [texte imprimé] / Alireza Hekmat-Ardakan, Auteur ; Frank Ajersch, Auteur . - 2011 . - pp. 3422–3428. Métallurgie Langues : Anglais (eng) in Acta materialia > Vol. 58 N° 9 (Mai 2010) . - pp. 3422–3428 Mots-clés : Thermodynamic Factsage Aluminum alloys Eutectic solidification Magnesium Résumé : This paper presents the thermodynamic evaluation of A390 hypereutectic Al–Si alloy (Al–17% Si–4.5% Cu–0.5% Mg) and alloys up to 10% Mg, using the Factsage® software. Two critical compositions were detected at 4.2% and 7.2% Mg where the temperatures of the liquidus, the start of the binary and of the ternary eutectic reaction are changed. These critical compositions show differences in the formation of Mg2Si intermetallic particles during the solidification interval. For compositions up to 4.2% Mg, the Mg2Si intermetallic phase first appears in the ternary eutectic zone. With Mg contents between 4.2% and 7.2%, Mg2Si particle appears in both the binary and ternary eutectic reactions. Above 7.2% Mg, it solidifies as a primary phase and also during the binary and ternary reactions. The calculated liquid fraction vs. temperature curves also showed a decrease of the eutectic formation temperature (knee point temperature) with the addition of Mg content up to 4.2% Mg. This temperature becomes almost constant up to 10% Mg. The calculation of eutectic formation temperature shows a good agreement with differential scanning calorimetry (DSC) tests. DEWEY : 669 ISSN : 1359-6454 En ligne : http://www.sciencedirect.com/science/article/pii/S1359645410001035

Exemplaires

Code-barres	Cote	Support	Localisation	Section	Disponibilité
aucun exemplaire