Ecofriendly cold ramming paste for an aluminum electrolysis cell with furan resin as a binder / Lin Tian in Industrial & engineering chemistry research, Vol. 51 N° 17 (Mai 2012)  

Public ISBD [article]  inIndustrial & engineering chemistry research > Vol. 51 N° 17 (Mai 2012) . - pp. 6018–6024 Titre : Ecofriendly cold ramming paste for an aluminum electrolysis cell with furan resin as a binder Type de document : texte imprimé Auteurs : Lin Tian, Auteur ; Yang min Zhou, Auteur ; Gang Xie, Auteur Année de publication : 2012 Article en page(s) : pp. 6018–6024 Note générale : Industrial chemistry Langues : Anglais (eng) Mots-clés : Electrolysis cell Résumé : Cold ramming paste was synthesized with electro-calcined anthracite (ECA) and artificial graphite as an aggregate and furan resin as a binder. Properties of synthesized paste were investigated by Universal Testing Machine, thermogravimetry (TG) and gas chromatography (GC) mass spectrometry (MS). The results show that the synthesized paste is an ecofriendly material and that it has some superior physical properties such as low electrical resistivity, high compressive strength, appropriate sodium penetration, and thermal expansion, all of which can meet industry requirements. The TG curve of the paste can be divided into three stages and the lower heating rate should be used in the second stage. Moreover, the resin functional groups disappear more completely at higher carbonized temperature based on infrared (IR) spectrum analysis. ISSN : 0888-5885 En ligne : http://pubs.acs.org/doi/abs/10.1021/ie202191y [article] Ecofriendly cold ramming paste for an aluminum electrolysis cell with furan resin as a binder [texte imprimé] / Lin Tian, Auteur ; Yang min Zhou, Auteur ; Gang Xie, Auteur . - 2012 . - pp. 6018–6024. Industrial chemistry Langues : Anglais (eng) in Industrial & engineering chemistry research > Vol. 51 N° 17 (Mai 2012) . - pp. 6018–6024 Mots-clés : Electrolysis cell Résumé : Cold ramming paste was synthesized with electro-calcined anthracite (ECA) and artificial graphite as an aggregate and furan resin as a binder. Properties of synthesized paste were investigated by Universal Testing Machine, thermogravimetry (TG) and gas chromatography (GC) mass spectrometry (MS). The results show that the synthesized paste is an ecofriendly material and that it has some superior physical properties such as low electrical resistivity, high compressive strength, appropriate sodium penetration, and thermal expansion, all of which can meet industry requirements. The TG curve of the paste can be divided into three stages and the lower heating rate should be used in the second stage. Moreover, the resin functional groups disappear more completely at higher carbonized temperature based on infrared (IR) spectrum analysis. ISSN : 0888-5885 En ligne : http://pubs.acs.org/doi/abs/10.1021/ie202191y

Exemplaires

Code-barres	Cote	Support	Localisation	Section	Disponibilité
aucun exemplaire