Effect of long-period stacking ordered phase on mechanical properties of Mg97Zn1Y2 extruded alloy / K. Hagihara in Acta materialia, Vol. 58 N° 19 (Novembre 2010)  

Public ISBD [article]  inActa materialia > Vol. 58 N° 19 (Novembre 2010) . - pp. 6282–6293 Titre : Effect of long-period stacking ordered phase on mechanical properties of Mg97Zn1Y2 extruded alloy Type de document : texte imprimé Auteurs : K. Hagihara, Auteur ; A. Kinoshita, Auteur ; Y. Sugino, Auteur Année de publication : 2011 Article en page(s) : pp. 6282–6293 Note générale : Métallurgie Langues : Anglais (eng) Mots-clés : Plastic deformation Magnesium alloys Extrusion Fiber-reinforced composites Intermetallic compounds Résumé : The mechanical properties of Mg97Zn1Y2 extruded alloy, composed of Mg matrix phase and a long-period stacking ordered phase, the so-called LPSO phase, with a volume fraction of approximately 24%, were investigated using compression tests at room temperature. The microstructure was varied to a large degree by various heat treatments at high temperatures above 400 °C, and the relationship between the microstructure and mechanical properties was clarified. The plastic behavior of the Mg/LPSO two-phase alloy was compared with that of Mg99.2Zn0.2Y0.6 alloy, composed almost Mg-solid-solution phase, and the strengthening mechanisms at work in the Mg97Zn1Y2 extruded alloy are discussed. The existence of the LPSO phase strongly enhanced the refinement of Mg matrix grains during extrusion, which led to a large increase in yield stress through the Hall–Petch relationship. In addition, the LPSO phases, which were aligned along the direction of extrusion in the Mg97Zn1Y2 extruded alloy, acted as hardening phases, being roughly coordinated with the short-fiber reinforcement mechanism. DEWEY : 669 ISSN : 1359-6454 En ligne : http://www.sciencedirect.com/science/article/pii/S1359645410004945 [article] Effect of long-period stacking ordered phase on mechanical properties of Mg97Zn1Y2 extruded alloy [texte imprimé] / K. Hagihara, Auteur ; A. Kinoshita, Auteur ; Y. Sugino, Auteur . - 2011 . - pp. 6282–6293. Métallurgie Langues : Anglais (eng) in Acta materialia > Vol. 58 N° 19 (Novembre 2010) . - pp. 6282–6293 Mots-clés : Plastic deformation Magnesium alloys Extrusion Fiber-reinforced composites Intermetallic compounds Résumé : The mechanical properties of Mg97Zn1Y2 extruded alloy, composed of Mg matrix phase and a long-period stacking ordered phase, the so-called LPSO phase, with a volume fraction of approximately 24%, were investigated using compression tests at room temperature. The microstructure was varied to a large degree by various heat treatments at high temperatures above 400 °C, and the relationship between the microstructure and mechanical properties was clarified. The plastic behavior of the Mg/LPSO two-phase alloy was compared with that of Mg99.2Zn0.2Y0.6 alloy, composed almost Mg-solid-solution phase, and the strengthening mechanisms at work in the Mg97Zn1Y2 extruded alloy are discussed. The existence of the LPSO phase strongly enhanced the refinement of Mg matrix grains during extrusion, which led to a large increase in yield stress through the Hall–Petch relationship. In addition, the LPSO phases, which were aligned along the direction of extrusion in the Mg97Zn1Y2 extruded alloy, acted as hardening phases, being roughly coordinated with the short-fiber reinforcement mechanism. DEWEY : 669 ISSN : 1359-6454 En ligne : http://www.sciencedirect.com/science/article/pii/S1359645410004945

Exemplaires

Code-barres	Cote	Support	Localisation	Section	Disponibilité
aucun exemplaire