Titre :	Toward a Physical Damage Variable for Concrete
Titre original :	Vers une Variable Physique de Dommages pour le Béton
Type de document :	texte imprimé
Auteurs :	Landis, Eric N., Auteur ; Gavin, Henri P., Éditeur scientifique
Année de publication :	2006
Article en page(s) :	771-774 p.
Note générale :	Génie Mécanique
Langues :	Anglais (eng)
Mots-clés :	Concrete Micro-structures Damage Fracture Radiographie Concret Dommages Rupture
Index. décimale :	621.34
Résumé :	Continuum damage mechanics models, while elegant and useful, suffer from what are typically highly idealized relationships between model and material. In this technical note, using three-dimensional (3D) measurements of internal cracking, direct, albeit simple relationships were made between the quantity of cracking and a corresponding scalar damage variable. Geometric properties of internal cracks were measured through 3D image analysis of in situ microtomographic scans of small concrete specimens subject to compression. A scalar damage variable was determined from the changes in stiffness measured in successive loading cycles. Results showed a nearly linear relationship between the damage variable and the volume of new cracks formed. In contrast, results showed a nonlinear relationship between the damage variable and the crack surface area. Such relationships can potentially lead to a more physical basis for continuum damage formulations. Les modèles de mécanique de dommages de continuum, tandis qu'élégants et utiles, souffrent de ce qui sont des rapports en général fortement idéalisés entre le modèle et le matériel. Dans cette note technique, en utilisant les mesures (3D) tridimensionnelles de fendre interne, directes, quoique des rapports simples ont été faits entre la quantité de fendre et une variable scalaire correspondante de dommages. Des propriétés géométriques des fissures internes ont été mesurées par l'analyse d'image 3D des balayages microtomographic in situ de petits spécimens concrets sujet à la compression. Une variable scalaire de dommages a été déterminée à partir des changements de la rigidité mesurée dans les cycles successifs de chargement. Les résultats ont montré que un rapport presque linéaire entre les dommages variables et le volume de nouvelles fissures a formé. En revanche, les résultats ont montré un rapport non-linéaire entre les dommages variables et la superficie de fente. De tels rapports peuvent potentiellement mener à une base plus physique pour des formulations de dommages de continuum.
En ligne :	landis@maine.edu

[article] Toward a Physical Damage Variable for Concrete = Vers une Variable Physique de Dommages pour le Béton [texte imprimé] / Landis, Eric N., Auteur ; Gavin, Henri P., Éditeur scientifique . - 2006 . - 771-774 p.
Génie Mécanique
Langues : Anglais (eng)
in Journal of engineering mechanics > Vol. 132 N°7 (Juillet 2006) . - 771-774 p.

Mots-clés :	Concrete Micro-structures Damage Fracture Radiographie Concret Dommages Rupture
Index. décimale :	621.34
Résumé :	Continuum damage mechanics models, while elegant and useful, suffer from what are typically highly idealized relationships between model and material. In this technical note, using three-dimensional (3D) measurements of internal cracking, direct, albeit simple relationships were made between the quantity of cracking and a corresponding scalar damage variable. Geometric properties of internal cracks were measured through 3D image analysis of in situ microtomographic scans of small concrete specimens subject to compression. A scalar damage variable was determined from the changes in stiffness measured in successive loading cycles. Results showed a nearly linear relationship between the damage variable and the volume of new cracks formed. In contrast, results showed a nonlinear relationship between the damage variable and the crack surface area. Such relationships can potentially lead to a more physical basis for continuum damage formulations. Les modèles de mécanique de dommages de continuum, tandis qu'élégants et utiles, souffrent de ce qui sont des rapports en général fortement idéalisés entre le modèle et le matériel. Dans cette note technique, en utilisant les mesures (3D) tridimensionnelles de fendre interne, directes, quoique des rapports simples ont été faits entre la quantité de fendre et une variable scalaire correspondante de dommages. Des propriétés géométriques des fissures internes ont été mesurées par l'analyse d'image 3D des balayages microtomographic in situ de petits spécimens concrets sujet à la compression. Une variable scalaire de dommages a été déterminée à partir des changements de la rigidité mesurée dans les cycles successifs de chargement. Les résultats ont montré que un rapport presque linéaire entre les dommages variables et le volume de nouvelles fissures a formé. En revanche, les résultats ont montré un rapport non-linéaire entre les dommages variables et la superficie de fente. De tels rapports peuvent potentiellement mener à une base plus physique pour des formulations de dommages de continuum.