Documents disponibles écrits par cet auteur

Surface corrosion of steel fibre reinforced concrete / S. U. Balouch in Cement and concrete research, Vol. 40 N° 3 (Mars 2010) 

Public ISBD [article]  in Cement and concrete research > Vol. 40 N° 3 (Mars 2010) . - pp. 410–414 Titre : Surface corrosion of steel fibre reinforced concrete Type de document : texte imprimé Auteurs : S. U. Balouch, Auteur ; J.P. Forth, Auteur Année de publication : 2012 Article en page(s) : pp. 410–414 Note générale : Bibliogr. Langues : Anglais (eng) Mots-clés : Fibre  reinforcement  ;  Concrete  skin;  Corrosion  ;  Durability Résumé : Corrosion of SFRC (Steel Fibre Reinforced Concrete) in an adverse environment, less harmful as compared to corrosion of steel reinforced concrete, is often considered to be of minor importance, however it exists. It can affect the fibres bridging the cracks and then decrease the strength of the concerned structures. As well, it results in the appearance of corrosion spots at exposed surfaces. Then the damaging effect is no longer expressed in terms of resistance, it is only aesthetic. It is especially undesirable in prefabricated structures. The work developed in this paper focuses on this second point: surface corrosion. Fibre reinforced concrete prisms have been subjected to cycles of salt fog (1 week) and drying (1 week). The results obtained demonstrate that with high W/C ratio (0.78), all the fibres which are embedded in concrete less than 1 mm are susceptible to give corrosion spots at the surface. When W/C is reduced to about 0.5, the minimum necessary cover to prevent surface corrosion drops to 1/10 mm or 2/10 mm and further decrease of W/C does not bring extra significant benefit. This result is in agreement with the analysis, by mercury intrusion, of the skin concrete porosity. It confirms a sharp change in the pore diameters when W/C is decreased from 0.78 to 0.48 and a quasi stability when it is varied from 0.48 to 0.36. Le travail présenté dans cet article est centré sur ce second point : la corrosion de surface. Des prismes de BFM ont été soumis à des cycles d'une semaine de brouillard salin alternant avec une semaine de séchage. Il en ressort que dans un béton de rapport E/C élevé (0,78), toutes les fibres enrobées de moins 1 mm sont susceptibles de donner naissance à des taches de rouille en surface. Lorsque E/C est réduit à environ 0,5, l'enrobage minimum nécessaire pour se prémunir de la corrosion de surface chute à 1/10 ou 2/10 mm et toute diminution supplémentaire de E/C n'apporte pas de bénéfice significatif. Ce résultat est en accord avec l'analyse porosimétrique du béton de peau. En effet, celle-ci confirme une chute importante du diamètre des pores lorsque E/C passe de 0,78 à 0,48 et une stabilités lorsqu'il est ensuite diminué jusqu'à 0,36. En ligne : http://www.sciencedirect.com/science/article/pii/S0008884609002841 [article] Surface corrosion of steel fibre reinforced concrete [texte imprimé] / S. U. Balouch, Auteur ; J.P. Forth, Auteur . - 2012 . - pp. 410–414. Bibliogr. Langues : Anglais (eng) in Cement and concrete research > Vol. 40 N° 3 (Mars 2010) . - pp. 410–414 Mots-clés : Fibre  reinforcement  ;  Concrete  skin;  Corrosion  ;  Durability Résumé : Corrosion of SFRC (Steel Fibre Reinforced Concrete) in an adverse environment, less harmful as compared to corrosion of steel reinforced concrete, is often considered to be of minor importance, however it exists. It can affect the fibres bridging the cracks and then decrease the strength of the concerned structures. As well, it results in the appearance of corrosion spots at exposed surfaces. Then the damaging effect is no longer expressed in terms of resistance, it is only aesthetic. It is especially undesirable in prefabricated structures. The work developed in this paper focuses on this second point: surface corrosion. Fibre reinforced concrete prisms have been subjected to cycles of salt fog (1 week) and drying (1 week). The results obtained demonstrate that with high W/C ratio (0.78), all the fibres which are embedded in concrete less than 1 mm are susceptible to give corrosion spots at the surface. When W/C is reduced to about 0.5, the minimum necessary cover to prevent surface corrosion drops to 1/10 mm or 2/10 mm and further decrease of W/C does not bring extra significant benefit. This result is in agreement with the analysis, by mercury intrusion, of the skin concrete porosity. It confirms a sharp change in the pore diameters when W/C is decreased from 0.78 to 0.48 and a quasi stability when it is varied from 0.48 to 0.36. Le travail présenté dans cet article est centré sur ce second point : la corrosion de surface. Des prismes de BFM ont été soumis à des cycles d'une semaine de brouillard salin alternant avec une semaine de séchage. Il en ressort que dans un béton de rapport E/C élevé (0,78), toutes les fibres enrobées de moins 1 mm sont susceptibles de donner naissance à des taches de rouille en surface. Lorsque E/C est réduit à environ 0,5, l'enrobage minimum nécessaire pour se prémunir de la corrosion de surface chute à 1/10 ou 2/10 mm et toute diminution supplémentaire de E/C n'apporte pas de bénéfice significatif. Ce résultat est en accord avec l'analyse porosimétrique du béton de peau. En effet, celle-ci confirme une chute importante du diamètre des pores lorsque E/C passe de 0,78 à 0,48 et une stabilités lorsqu'il est ensuite diminué jusqu'à 0,36. En ligne : http://www.sciencedirect.com/science/article/pii/S0008884609002841