Documents disponibles écrits par cet auteur

Toughening of polyamide - 6 with a maleic anhydride functionalized acrylonitrile - styrene - butyl acrylate copolymer / Zhenguo Liu in Industrial & engineering chemistry research, Vol. 51 N° 27 (Juillet 2012) 

Public ISBD [article]  in Industrial & engineering chemistry research > Vol. 51 N° 27 (Juillet 2012) . - pp. 9235-9240 Titre : Toughening of polyamide - 6 with a maleic anhydride functionalized acrylonitrile - styrene - butyl acrylate copolymer Type de document : texte imprimé Auteurs : Zhenguo Liu, Auteur ; Yunjiao Deng, Auteur ; Ye Han, Auteur Année de publication : 2012 Article en page(s) : pp. 9235-9240 Note générale : Industrial chemistry Langues : Anglais (eng) Mots-clés : Polyamide Résumé : Maleic anhydride (MAH) functionalized acrylate-styrene-acrylonitrile (ASA) copolymers (F-ASA) were prepared via an emulsion polymerization process. The F-ASA particles were used to toughen Polyamide-6 (PA-6). Molau tests showed the compatibilization reactions between PA-6 and F-ASA. The notched impact strength of PA-6 was effectively improved by the use of F-ASA. At a rubber content of 20% by weight in PA-6/F-ASA blends, it was found that the impact strength increased with the MAH content. When the MAH content was 8% in F-ASA, the impact strength was 1008 J/m. The influence of rubber content on the properties of PA-6/F-ASA8 blends was investigated. The results showed that brittle-ductile transition took place when the rubber content was 20%. Moreover, increasing the MAH content of the blends reduced the brittle-ductile temperature of the F-ASA/PA-6 blends from 50 °C to about 0 °C. Scanning electron microscopy (SEM) results showed that cavitation of rubber particles and shear yielding of the PA-6 matrix were the major toughening mechanisms. ISSN : 0888-5885 En ligne : http://pubs.acs.org/doi/abs/10.1021/ie202960q [article] Toughening of polyamide - 6 with a maleic anhydride functionalized acrylonitrile - styrene - butyl acrylate copolymer [texte imprimé] / Zhenguo Liu, Auteur ; Yunjiao Deng, Auteur ; Ye Han, Auteur . - 2012 . - pp. 9235-9240. Industrial chemistry Langues : Anglais (eng) in Industrial & engineering chemistry research > Vol. 51 N° 27 (Juillet 2012) . - pp. 9235-9240 Mots-clés : Polyamide Résumé : Maleic anhydride (MAH) functionalized acrylate-styrene-acrylonitrile (ASA) copolymers (F-ASA) were prepared via an emulsion polymerization process. The F-ASA particles were used to toughen Polyamide-6 (PA-6). Molau tests showed the compatibilization reactions between PA-6 and F-ASA. The notched impact strength of PA-6 was effectively improved by the use of F-ASA. At a rubber content of 20% by weight in PA-6/F-ASA blends, it was found that the impact strength increased with the MAH content. When the MAH content was 8% in F-ASA, the impact strength was 1008 J/m. The influence of rubber content on the properties of PA-6/F-ASA8 blends was investigated. The results showed that brittle-ductile transition took place when the rubber content was 20%. Moreover, increasing the MAH content of the blends reduced the brittle-ductile temperature of the F-ASA/PA-6 blends from 50 °C to about 0 °C. Scanning electron microscopy (SEM) results showed that cavitation of rubber particles and shear yielding of the PA-6 matrix were the major toughening mechanisms. ISSN : 0888-5885 En ligne : http://pubs.acs.org/doi/abs/10.1021/ie202960q