Development of al-alloy coating for advanced nuclear systems using lead alloys / Yuji Kurata in Transactions of the ASME . Journal of engineering for gas turbines and power, Vol. 134 N° 6 (Juin 2012)  

Public ISBD [article]  inTransactions of the ASME . Journal of engineering for gas turbines and power > Vol. 134 N° 6 (Juin 2012) . - 07 p. Titre : Development of al-alloy coating for advanced nuclear systems using lead alloys Type de document : texte imprimé Auteurs : Yuji Kurata, Auteur ; Hitoshi Yokota, Auteur ; Tetsuya Suzuki, Auteur Année de publication : 2012 Article en page(s) : 07 p. Note générale : Génie mécanique Langues : Anglais (eng) Mots-clés : Al-alloy Nuclear systems Lead alloys Index. décimale : 620.1 Essais des matériaux. Défauts des matériaux. Protection des matériaux Résumé : Small and medium reactors using lead alloys as coolants are one of the promising reactor concepts with improved safety because of their thermal-physical and chemical properties. This paper focuses on the development of Al-alloy coating for nuclear systems using liquid lead-bismuth eutectic (LBE). Since corrosion attack becomes severe against structural steels at high temperatures in liquid LBE, it is necessary to improve the corrosion resistance of steels. An Al-alloy coating method using Al, Ti, and Fe powders, and laser beam heating has been developed. The main defects formed in the Al-powder-alloy coating process are surface defects and cracks. The conditions required to avoid these defects are the employment of the laser beam scanning rate of 20 mm/min and the adjustment of the Al concentration in the coating layer. According to the results of the corrosion tests at 550°C in liquid LBE, the Al-alloy coating layers on 316SS prevent severe corrosion attack such as grain boundary corrosion and LBE penetration observed in the 316SS without coating. The good corrosion resistance of the Al-alloy coating is based on the thin Al-oxide film, which can be regenerated in liquid LBE. From the viewpoint of the soundness of the produced Al-powder-alloy coating layers and the preservation of their corrosion resistance, it is estimated that the range of adequate Al concentration in the coating layer is from 4 to 12 wt. %. DEWEY : 620.1 ISSN : 0742-4795 En ligne : http://asmedl.org/getabs/servlet/GetabsServlet?prog=normal&id=JETPEZ000134000006 [...] [article] Development of al-alloy coating for advanced nuclear systems using lead alloys [texte imprimé] / Yuji Kurata, Auteur ; Hitoshi Yokota, Auteur ; Tetsuya Suzuki, Auteur . - 2012 . - 07 p. Génie mécanique Langues : Anglais (eng) in Transactions of the ASME . Journal of engineering for gas turbines and power > Vol. 134 N° 6 (Juin 2012) . - 07 p. Mots-clés : Al-alloy Nuclear systems Lead alloys Index. décimale : 620.1 Essais des matériaux. Défauts des matériaux. Protection des matériaux Résumé : Small and medium reactors using lead alloys as coolants are one of the promising reactor concepts with improved safety because of their thermal-physical and chemical properties. This paper focuses on the development of Al-alloy coating for nuclear systems using liquid lead-bismuth eutectic (LBE). Since corrosion attack becomes severe against structural steels at high temperatures in liquid LBE, it is necessary to improve the corrosion resistance of steels. An Al-alloy coating method using Al, Ti, and Fe powders, and laser beam heating has been developed. The main defects formed in the Al-powder-alloy coating process are surface defects and cracks. The conditions required to avoid these defects are the employment of the laser beam scanning rate of 20 mm/min and the adjustment of the Al concentration in the coating layer. According to the results of the corrosion tests at 550°C in liquid LBE, the Al-alloy coating layers on 316SS prevent severe corrosion attack such as grain boundary corrosion and LBE penetration observed in the 316SS without coating. The good corrosion resistance of the Al-alloy coating is based on the thin Al-oxide film, which can be regenerated in liquid LBE. From the viewpoint of the soundness of the produced Al-powder-alloy coating layers and the preservation of their corrosion resistance, it is estimated that the range of adequate Al concentration in the coating layer is from 4 to 12 wt. %. DEWEY : 620.1 ISSN : 0742-4795 En ligne : http://asmedl.org/getabs/servlet/GetabsServlet?prog=normal&id=JETPEZ000134000006 [...]

Exemplaires

Code-barres	Cote	Support	Localisation	Section	Disponibilité
aucun exemplaire