[article]
| Titre : |
Ex situ TEM observation of localized attack on AA 6061 |
| Type de document : |
texte imprimé |
| Auteurs : |
D. M. Sun, Auteur ; Y. M. Jiang, Auteur ; Q. W. Xiang, Auteur |
| Année de publication : |
2010 |
| Article en page(s) : |
pp. 105–110 |
| Note générale : |
Génie mécanique |
| Langues : |
Anglais (eng) |
| Mots-clés : |
Aluminum alloy 6061 localized corrosion transmission electron microscopy |
| Résumé : |
Ex situ transmission electron microscopy (TEM) was used in conjunction with energy dispersed spectrometry (EDS) to monitor evolution near the pre-selected inclusions during initial stages of localized dissolution on the aluminum alloy (AA) 6061 immersed in 0.1 M NaCl solution. On the alloy TEM foil, Mg2Si phase particles were observed to preferentially dissolve after 3 min immersion. Nevertheless, different dissolution behaviors were observed to form in the vicinities of the different structure Fe-rich precipitates; the trenches were observed near the anorthic phase particle, but no obvious priority dissolution was detected in the vicinity of hexagonal phase particles. The preferential sites of alloy dissolution were found to depend on both the component and the structure of the intermetallics. The shift of electrochemical potential was found to relate the dissolution of the heterogeneous phases. |
| En ligne : |
http://onlinelibrary.wiley.com/doi/10.1002/maco.200905267/abstract |
in Materials and corrosion > Vol. 61 N° 2 (Fevrier 2010) . - pp. 105–110
[article] Ex situ TEM observation of localized attack on AA 6061 [texte imprimé] / D. M. Sun, Auteur ; Y. M. Jiang, Auteur ; Q. W. Xiang, Auteur . - 2010 . - pp. 105–110. Génie mécanique Langues : Anglais ( eng) in Materials and corrosion > Vol. 61 N° 2 (Fevrier 2010) . - pp. 105–110
| Mots-clés : |
Aluminum alloy 6061 localized corrosion transmission electron microscopy |
| Résumé : |
Ex situ transmission electron microscopy (TEM) was used in conjunction with energy dispersed spectrometry (EDS) to monitor evolution near the pre-selected inclusions during initial stages of localized dissolution on the aluminum alloy (AA) 6061 immersed in 0.1 M NaCl solution. On the alloy TEM foil, Mg2Si phase particles were observed to preferentially dissolve after 3 min immersion. Nevertheless, different dissolution behaviors were observed to form in the vicinities of the different structure Fe-rich precipitates; the trenches were observed near the anorthic phase particle, but no obvious priority dissolution was detected in the vicinity of hexagonal phase particles. The preferential sites of alloy dissolution were found to depend on both the component and the structure of the intermetallics. The shift of electrochemical potential was found to relate the dissolution of the heterogeneous phases. |
| En ligne : |
http://onlinelibrary.wiley.com/doi/10.1002/maco.200905267/abstract |
|
Ajouter le résultat dans votre panier Faire une suggestion Affiner la rechercheEx situ TEM observation of localized attack on AA 6061 in Materials and corrosion, Vol. 61 N° 2 (Fevrier 2010)