Documents disponibles écrits par cet auteur

Impeding corrosion of sintered NdFeB magnets with titanium nitride coating / A. Ali in Materials and corrosion, Vol. 61 N° 2 (Fevrier 2010) 

Public ISBD [article]  in Materials and corrosion > Vol. 61 N° 2 (Fevrier 2010) . - pp. 130–135 Titre : Impeding corrosion of sintered NdFeB magnets with titanium nitride coating Type de document : texte imprimé Auteurs : A. Ali, Auteur ; A. Ahmad, Auteur ; K. M. Deen, Auteur Année de publication : 2010 Article en page(s) : pp. 130–135 Note générale : Génie mécanique Langues : Anglais (eng) Mots-clés : Electrochemical  impedance  spectroscopy;  pits  re-passivation;  sintered  NdFeB  Magnets Résumé : Sintered NdFeB magnets have poor corrosion resistance that renders them susceptible to corrosion in industrial and marine environments. This paper evaluates the properties of cathodic arc physical vapour deposited (CAPVD) titanium nitride coating for corrosion protection of sintered NdFeB permanent magnets. The performance of titanium nitride coating has been compared to the electrodeposited nickel–copper–nickel multilayer coating. The rates of coatings degradation in simulated marine environment were estimated with electrochemical impedance spectroscopy (EIS). Cyclic polarization was carried out to assess the pitting potential. The surface chemistry and coating morphologies were studied with scanning electron microscope (SEM). X-ray diffraction (XRD) was used for qualitative phase analyses of coatings and the substrate. It was figured out that the charge transfer resistance of CAPVD titanium nitride coating increased with exposure time. The negative rate of Rp-degradation for titanium nitride coating compared to the nickel–copper–nickel multilayer for equivalent exposure time is a unique and valuable result. Polarization results showed that ‘pits re-passivation’ of titanium nitride coating could be responsible for the extended corrosion protection of the NdFeB substrate. The magnetic properties remained comparable for both types of coatings. En ligne : http://onlinelibrary.wiley.com/doi/10.1002/maco.200905265/abstract [article] Impeding corrosion of sintered NdFeB magnets with titanium nitride coating [texte imprimé] / A. Ali, Auteur ; A. Ahmad, Auteur ; K. M. Deen, Auteur . - 2010 . - pp. 130–135. Génie mécanique Langues : Anglais (eng) in Materials and corrosion > Vol. 61 N° 2 (Fevrier 2010) . - pp. 130–135 Mots-clés : Electrochemical  impedance  spectroscopy;  pits  re-passivation;  sintered  NdFeB  Magnets Résumé : Sintered NdFeB magnets have poor corrosion resistance that renders them susceptible to corrosion in industrial and marine environments. This paper evaluates the properties of cathodic arc physical vapour deposited (CAPVD) titanium nitride coating for corrosion protection of sintered NdFeB permanent magnets. The performance of titanium nitride coating has been compared to the electrodeposited nickel–copper–nickel multilayer coating. The rates of coatings degradation in simulated marine environment were estimated with electrochemical impedance spectroscopy (EIS). Cyclic polarization was carried out to assess the pitting potential. The surface chemistry and coating morphologies were studied with scanning electron microscope (SEM). X-ray diffraction (XRD) was used for qualitative phase analyses of coatings and the substrate. It was figured out that the charge transfer resistance of CAPVD titanium nitride coating increased with exposure time. The negative rate of Rp-degradation for titanium nitride coating compared to the nickel–copper–nickel multilayer for equivalent exposure time is a unique and valuable result. Polarization results showed that ‘pits re-passivation’ of titanium nitride coating could be responsible for the extended corrosion protection of the NdFeB substrate. The magnetic properties remained comparable for both types of coatings. En ligne : http://onlinelibrary.wiley.com/doi/10.1002/maco.200905265/abstract