Electrochemical methods study on corrosion of 5% Al–Zn alloy-coated steel under thin electrolyte layers / S. Xing in Materials and corrosion, Vol. 61 N° 5 (Mai 2010)  

Public ISBD [article]  inMaterials and corrosion > Vol. 61 N° 5 (Mai 2010) . - pp. 428–431 Titre : Electrochemical methods study on corrosion of 5% Al–Zn alloy-coated steel under thin electrolyte layers Type de document : texte imprimé Auteurs : S. Xing, Auteur ; Y. Li, Auteur ; J. Wu, Auteur Année de publication : 2010 Article en page(s) : pp. 428–431 Note générale : Génie mécanique Langues : Anglais (eng) Mots-clés : 5% Al–Zn  corrosion monitoring  electrochemical impedance spectroscopy  wet–dry condition Résumé : The corrosion behavior of a 5% Al–Zn alloy (GF) coated steel was investigated under cyclic wet–dry condition using electrochemical techniques. The wet–dry cycle was conducted by exposure to alternate condition of 1 h immersion in seawater and 7 h drying at ambient temperature. The polarization resistance, Rp of the coating was monitored during the wet–dry cycles by two points AC impedance method and the corrosion potential, Ecorr was measured only when the coating was immersed in seawater. Simultaneously, the electrochemical impedance spectroscopy (EIS) of the coating was obtained after it was immersed in different cycles of wet–dry condition. The results obtained by two points AC impedance method had good agreement with those achieved from EIS technique, which proved that the two points AC impedance method was correct and an effective method for atmospheric corrosion study. The monitoring results indicated that the corrosion rate of GF coating firstly increased, then decreased slowly with time, and at last reached a relative steady state with local corrosion under the cyclic wet–dry alternate condition. En ligne : http://onlinelibrary.wiley.com/doi/10.1002/maco.200905313/abstract [article] Electrochemical methods study on corrosion of 5% Al–Zn alloy-coated steel under thin electrolyte layers [texte imprimé] / S. Xing, Auteur ; Y. Li, Auteur ; J. Wu, Auteur . - 2010 . - pp. 428–431. Génie mécanique Langues : Anglais (eng) in Materials and corrosion > Vol. 61 N° 5 (Mai 2010) . - pp. 428–431 Mots-clés : 5% Al–Zn  corrosion monitoring  electrochemical impedance spectroscopy  wet–dry condition Résumé : The corrosion behavior of a 5% Al–Zn alloy (GF) coated steel was investigated under cyclic wet–dry condition using electrochemical techniques. The wet–dry cycle was conducted by exposure to alternate condition of 1 h immersion in seawater and 7 h drying at ambient temperature. The polarization resistance, Rp of the coating was monitored during the wet–dry cycles by two points AC impedance method and the corrosion potential, Ecorr was measured only when the coating was immersed in seawater. Simultaneously, the electrochemical impedance spectroscopy (EIS) of the coating was obtained after it was immersed in different cycles of wet–dry condition. The results obtained by two points AC impedance method had good agreement with those achieved from EIS technique, which proved that the two points AC impedance method was correct and an effective method for atmospheric corrosion study. The monitoring results indicated that the corrosion rate of GF coating firstly increased, then decreased slowly with time, and at last reached a relative steady state with local corrosion under the cyclic wet–dry alternate condition. En ligne : http://onlinelibrary.wiley.com/doi/10.1002/maco.200905313/abstract

Exemplaires

Code-barres	Cote	Support	Localisation	Section	Disponibilité
aucun exemplaire