Fabrication of mesoporous silica coating by electrophoretic deposimtion / Hideyuki Negishi in Industrial & engineering chemistry research, Vol. 47 N°19 (Octobre 2008)  

Public ISBD [article]  inIndustrial & engineering chemistry research > Vol. 47 N°19 (Octobre 2008) . - p. 7236–7241 Titre : Fabrication of mesoporous silica coating by electrophoretic deposimtion Type de document : texte imprimé Auteurs : Hideyuki Negishi, Auteur ; Akira Endo, Auteur ; Takao Ohmori, Auteur Année de publication : 2008 Article en page(s) : p. 7236–7241 Note générale : Chemical engineering Langues : Anglais (eng) Mots-clés : Applying electrophoretic deposition Mesoporous silicate Spray-drying method Résumé : The technological feasibility of applying electrophoretic deposition (EPD) to ordered mesoporous silicate (MPS) powder has been studied. The EPD technique was investigated for the fabrication of an MPS thick film using MPS synthesized by the spray-drying method. It was found that the MPS powder deposition rate was low with an alcohol EPD bath and very high with an acetone EPD bath. The deposition amount could be easily controlled by changing the MPS powder concentration, the applied dc voltage, and the deposition time. An MPS particle/acetone suspension in which the particles were negatively charged showed the highest deposition rate among the tested organic solvents. MPS powder was deposited by EPD at 50 V for 10 min onto a tubular stainless steel substrate, and a uniform coating approximately 250 μm in thickness was obtained. After heat treatment at 573 K, the MPS powder could be fixed on the substrate without the addition of binders. The obtained MPS thick film had the same porous structure and nitrogen and water vapor adsorption properties as the parent MPS powder. En ligne : http://pubs.acs.org/doi/abs/10.1021/ie071473i [article] Fabrication of mesoporous silica coating by electrophoretic deposimtion [texte imprimé] / Hideyuki Negishi, Auteur ; Akira Endo, Auteur ; Takao Ohmori, Auteur . - 2008 . - p. 7236–7241. Chemical engineering Langues : Anglais (eng) in Industrial & engineering chemistry research > Vol. 47 N°19 (Octobre 2008) . - p. 7236–7241 Mots-clés : Applying electrophoretic deposition Mesoporous silicate Spray-drying method Résumé : The technological feasibility of applying electrophoretic deposition (EPD) to ordered mesoporous silicate (MPS) powder has been studied. The EPD technique was investigated for the fabrication of an MPS thick film using MPS synthesized by the spray-drying method. It was found that the MPS powder deposition rate was low with an alcohol EPD bath and very high with an acetone EPD bath. The deposition amount could be easily controlled by changing the MPS powder concentration, the applied dc voltage, and the deposition time. An MPS particle/acetone suspension in which the particles were negatively charged showed the highest deposition rate among the tested organic solvents. MPS powder was deposited by EPD at 50 V for 10 min onto a tubular stainless steel substrate, and a uniform coating approximately 250 μm in thickness was obtained. After heat treatment at 573 K, the MPS powder could be fixed on the substrate without the addition of binders. The obtained MPS thick film had the same porous structure and nitrogen and water vapor adsorption properties as the parent MPS powder. En ligne : http://pubs.acs.org/doi/abs/10.1021/ie071473i

Exemplaires

Code-barres	Cote	Support	Localisation	Section	Disponibilité
aucun exemplaire