Facile fabrication and wettability of nestlike microstructure maintained mixed metal oxides films from layered double hydroxide films precursors / Hongyun Chen in Industrial & engineering chemistry research, Vol. 47 N°17 (Septembre 2008) 

Public ISBD [article]  in Industrial & engineering chemistry research > Vol. 47 N°17 (Septembre 2008) . - p. 6607–6611 Titre : Facile fabrication and wettability of nestlike microstructure maintained mixed metal oxides films from layered double hydroxide films precursors Type de document : texte imprimé Auteurs : Hongyun Chen, Auteur ; Fazhi Zhang, Auteur ; Sailong Xu, Auteur Année de publication : 2008 Article en page(s) : p. 6607–6611 Note générale : Chemical engineering Langues : Anglais (eng) Mots-clés : Mixed  metal  oxide  films  Nestlike  microstructure  LDH  film  precursors  Scanning  electron  microscopy Résumé : Mixed metal oxide (MMO) films containing Ni2+ and Al3+ have been fabricated by a simple process involving calcination of layered double hydroxide (LDH) film precursors at 300−600 °C for 4 h in air. Scanning electron microscopy (SEM) reveals that the resulting Ni/Al−O thin films maintain the original nestlike morphology of the precursor films without any deformation of the microstructure during the thermal decomposition process. After surface treatment with an aqueous solution of sodium laurate, the wettability of the NiAl-LDH and Ni/Al−O thin film surfaces changes from hydrophilic to hydrophobic. Moreover, whereas the NiAl-LDH film exhibits a low adhesion for water (Cassie−Baxter behavior) after surface modification, the Ni/Al−O films exhibit a high adhesion for water (Wenzel behavior). A possible explanation for this phenomenon has been suggested. En ligne : http://pubs.acs.org/doi/abs/10.1021/ie800388w [article] Facile fabrication and wettability of nestlike microstructure maintained mixed metal oxides films from layered double hydroxide films precursors [texte imprimé] / Hongyun Chen, Auteur ; Fazhi Zhang, Auteur ; Sailong Xu, Auteur . - 2008 . - p. 6607–6611. Chemical engineering Langues : Anglais (eng) in Industrial & engineering chemistry research > Vol. 47 N°17 (Septembre 2008) . - p. 6607–6611 Mots-clés : Mixed  metal  oxide  films  Nestlike  microstructure  LDH  film  precursors  Scanning  electron  microscopy Résumé : Mixed metal oxide (MMO) films containing Ni2+ and Al3+ have been fabricated by a simple process involving calcination of layered double hydroxide (LDH) film precursors at 300−600 °C for 4 h in air. Scanning electron microscopy (SEM) reveals that the resulting Ni/Al−O thin films maintain the original nestlike morphology of the precursor films without any deformation of the microstructure during the thermal decomposition process. After surface treatment with an aqueous solution of sodium laurate, the wettability of the NiAl-LDH and Ni/Al−O thin film surfaces changes from hydrophilic to hydrophobic. Moreover, whereas the NiAl-LDH film exhibits a low adhesion for water (Cassie−Baxter behavior) after surface modification, the Ni/Al−O films exhibit a high adhesion for water (Wenzel behavior). A possible explanation for this phenomenon has been suggested. En ligne : http://pubs.acs.org/doi/abs/10.1021/ie800388w